Independent Standard Test Results

TECHNICAL DATA

 

TECHNICAL DATA

Physical Properties

                       Product Type     Di-vinyl ester base, inert hard fillers and “                                                                 
                                            Universal colourants

                        Appearance     Dense paint-like consistency

                        Viscosity          10,000 to 15,000 cps

                         PH Level          9.0 to 9.5

Toxicity    Non –Toxic

Performance Characteristics

TEST              Standard                       Result

Surface Burning  :    CAN4-S102                     flame spread  -8

Characteristics   :    fuel contributed <5;smoke developed <5  

Dry adhesion:  Can/CGSB 1GP.162-M90  No Bond failure with axial of  222 newtons 

Water absorption : Can/CGSB 1GP.162-M90  3.78% by weight

                   Permeance    7.42 perms

                  
Accelerated weathering : Can/CGSB 1GP.162-M90  EXCELLENT

   Freeze-thaw stability :      Can/CGSB 1GP.162-M90  NO coagulations

                   Alkali resistance    :          Can/CGSB 1GP.162-M90  NO Change  
                         

Testing by an Independent Testing Laboratory found:

 IMPACT RESISTANCE

* Direct Impact Resistance: no visible signs of chipping, cracking detachment from the steel plate when a 2 lb. steel ball was dropped from 8 feet with the impact at the center of the specimen, coating exhibited firm adhesion outside the impact area.

* Gardner Impact Resistance; external/concave impact of a 70"/lb.; no damage

 SALT SPRAY RESISTANCE

* No evidence of rusting or blistering when exposed for a continuous 336 hours.

 RESISTANCE TO GASOLINE

* After 30 minutes immersion in gasoline, sample showed no wrinkling loss of adhesion. After subsequent drying for 2 hours, the film show no blistering, no softening and no noticeable discoloration.

 RESISTANCE TO ACIDS [Hydrochloric (HCl), Nitric (HN03), Sulfuric (H2SO4)

* No evidence of softening, blistering, wrinkling, loss of adhesion appreciable color change after 4 hours exposure.

 WATER RESISTANCE

* No evidence of blistering or wrinkling when immersed in water at 23 C for a continuous 18 hours.

 FLEXIBILITY

* Coating showed no loss of adhesion, cracking or peeling and no loss of its protective value when bent at 0 F (-18 C) through 360 F over a 1/8" diameter mandrel.

 ADHESION (KNIFE TEST)

* Class 5 - no evidence of flaking or loss of adhesion.

 ABRASION RESISTANCE (FALLING SAND METHOD)

* The coating exhibited excellent resistance to abrasion. After 136,000 g there was no visible wear-through.

 



Chiri Enterprise offers innovative products for: Commercial, Military, Industrial and Marine coating
applications; Residential: Driveway, Roof; Auto / Truck Muffler, truck bed liner, hockey stick and shoe, boot protection applications.

Chiri Enterprise Inc. 2004 - Innovative New Products - Coating applications - Coatings - Industrial - Marine - Military - Automotive